Influence of glass fiber posts and class III direct restorations on the resistance of anterior teeth / Influência dos pinos de fibra de vidro e restaurações diretas classe III na resistência dos dentes anteriores

This study objectives to evaluate the fracture strength of upper central incisors (UCI) restored with composite resin (CR) in Class III cavities and endodontically treated teeth with or without glass fiber post (GFP), analyzing their failure mode. Sixty human UCI were randomly divided into four experimental groups: endodontically treated teeth without GFP (G1), endodontically treated teeth with GFP (G2), teeth with mesial/distal Class III cavities restored with CR without GFP (G3), and teeth with mesial/distal Class III cavities restored with CR with GFP (G4). The samples were submitted to the fracture strength test in a universal testing machine with a compression shear load applied at speed of 1.0 mm/min until fracture occurred. The data were submitted to one-way ANOVA (α=0.05) and the samples were analyzed for failure mode. The analysis did not show a significant statistical difference in fracture strength between the groups (p>0.05). The results showed that only endodontically treated teeth (G1) (753.4N) presented behavior similar to teeth with GFP (G2) (702.1N). The same occurred when comparing teeth with Class III cavities without GFP (G3) (670.2 N) and with GFP (G4) (746.1N). It can be concluded that glass fiber posts do not change the fracture strength of incisors with endodontic treatment and Class III cavities.

Este estudo objetiva avaliar a resistência à fratura de incisivos centrais superiores (ICS) restaurados com resina composta (RC) em cavidades Classe III e dentes tratados endodonticamente com ou sem pino de fibra de vidro (PFV), analisando seu padrão de fratura. Sessenta ICS humanos foram divididos aleatoriamente em quatro grupos experimentais: dentes tratados endodonticamente sem PFV (G1), dentes tratados endodonticamente com PFV (G2), dentes com cavidades mesiais/distais Classe III restauradas com RC sem PFV (G3), e dentes com cavidades mesiais/distais Classe III restauradas com RC com PFV (G4). As amostras foram submetidas ao teste de resistência à fratura em uma máquina universal de ensaios com uma carga de cisalhamento de compressão aplicada na velocidade de 1,0 mm / min até a ocorrência da fratura. Os dados foram submetidos à ANOVA unidirecional (α=0,05) e as amostras foram analisadas quanto ao modo de falha. A análise não mostrou diferença estatisticamente significativa na resistência à fratura entre os grupos (p>0,05). Os resultados mostraram que os dentes apenas tratados endodonticamente (G1) (753,4N) apresentaram comportamento semelhante aos dentes com PFV (G2) (702,1N). O mesmo ocorreu ao comparar dentes com cavidades Classe III sem PFV (G3) (670.2 N) e com PFV (G4) (746.1N). Pode-se concluir que pinos de fibra de vidro não alteram a resistência à fratura de incisivos com tratamento endodôntico e cavidades Classe III.

Influence of remaining coronal structure and finish line on the fracture strength of roots restored with metallic posts

The purpose of this study was to evaluate the fracture strength of roots that were prosthetically restored with metallic posts with or without any remaining coronal structure and with different finish lines. Sixty bovine incisors were sectioned below the cementoenamel junction, endodontically treated, and randomly divided into six experimental groups (n = 10) containing teeth with or without any remaining coronal structure, and with a beveled shoulder, a bevel, or a shoulder finish line design. The metallic posts were luted with dual-cured resin cement. The cores were made with composite resin, and metal crowns were cemented with zinc phosphate cement. The specimens were subjected to a tangential compressive load (135º angle) at a crosshead speed of 0.5 mm/min until failure, using a universal testing machine. The fracture strength data were analyzed using the ANOVA and LSMeans (least square means) tests (α= 0.05). The data indicated that the teeth with 2 mm of remaining coronal structure showed the highest fracture strength values when compared with the teeth without any remaining structure (p < 0.05). As to the different finish line designs, the highest fracture strength values were obtained for the beveled shoulder, followed by the bevel and then by the shoulder designs (p < 0.05). It may be concluded that, to increase fracture strength, a beveled shoulder and 2 mm of remaining coronal structure are the ideal conditions.

Effect of endodontic irrigating solutions on the adhesive bond strength to dentin / Efeito de soluções irrigadoras endodônticas na resistência adesiva à dentina

PURPOSE: To evaluate the bond strength of a total-etching adhesive system to dentin irrigated with 1% sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid 17% (EDTA). METHODS: Thirty human molars were sectioned 3mm below the oclusal surface and were randomly divided into 3 groups (n=10): G1, no treatment (control); G2, 1% NaOCl; G3, NaOCl followed by EDTA. The specimens received the total-etching adhesive system, restored with microhybrid composite resin, sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile bond strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. G2 samples were not submitted to the test because they fractured just before testing, and its values were considered zero to the statistical analysis. RESULTS: The means and standard deviations (MPa) were: G1, 8.41 (±3.51); G2, 0.0 (±0.00); G3, 8.47 (±3.53). CONCLUSION: It was concluded that the application of the NaOCl irrigating solution significantly decreased the bond strength values. The use of NaOCl followed by EDTA resulted in bond strength values not statistically different from control group.

OBJETIVO: Avaliar a resistência de união de um sistema adesivo condicione-e-lave à dentina irrigada com hipoclorito de sódio 1% (NaOCl) e ácido etilenodiaminotetracético 17% (EDTA). METODOLOGIA: Trinta molares humanos foram seccionados 3mm abaixo da superficie oclusal e aleatoriamente divididos em 3 grupos (n=10): G1 (controle), nenhum tratamento; G2, NaOCl; G3, NaOCl seguido por EDTA. Os especimes foram hibridizados com um sistema adesivo condicione-e-lave, foram restaurados com resino composta microhibrida e seccionados de forma a originar 4 amplulhetas de cada dente. As fatias foram submetidas ao teste de resistência de união à microtraçnao em máquina universal de ensaios (EMIC DL 2000) à uma velocidade de 0,5 mm/min até o momento da fratura. Os resultados foram analisados estatisticamente por ANOVA seguido por Newman-Keuls. As amostras do G2 não foram submetidas aos testes de resistência de união pois fraturaram antes dos testes, e seus valores foram considerados zero para análise estatística. RESULTADOS: A média e desvios-padrão foram (MPa): G1 - 8,41 (±3,51); G2 - 0,0 (±0,00); e G3 - 8,47 (±3,53). CONCLUSÃO: Pode-se concluir que a irrigação com NaOCl diminui significativamente os valores de resistência de união. O uso de NaOCl seguido por EDTA resultaram em valores de resistência de união sem diferença estatística com o grupo controle.

Influence of ferrule preparation with or without glass fiber post on fracture resistance of endodontically treated teeth

OBJECTIVE: This study evaluated the effect of ferrule preparation (Fp) on the fracture resistance of endodontically treated teeth, restored with composite resin cores with or without glass fiber posts. MATERIAL AND METHODS: Forty-four bovine teeth were sectioned 19 or 17 mm (2 mm ferrule) from the apex, endodontically treated and assigned to four groups (n = 11): Group 1: Fp and post; Group 2: Fp and without post; Group 3: without Fp and with post; Group 4: without Fp and without post. All specimens were restored with composite resin core and metal crown. Specimens were subjected to fracture resistance testing in a universal testing machine at a crosshead speed of 0.5 mm/min. The data were analyzed by two-way ANOVA and Tukey's tests (α=0.05). RESULTS: The mean fracture resistance values were as follows: Group 1: 573.3 N; Group 2: 552.5 N; Group 3: 275.3 N; Group 4: 258.6 N. Significantly higher fracture resistance was found for the groups with Fp (p<0.001). CONCLUSION: There was no statistically significant interaction between the "Fp" and "post" factors (p = 0.954). The ferrule preparation increased the fracture resistance of endodontically treated teeth. However, the use of glass fiber post showed no significant influence on the fracture resistance.

Influence of sodium hypochlorite and edta on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. OBJECTIVE: The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (EDTA). MATERIAL AND METHODS: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1 percent NaOCl; and G3: 1 percent NaOCl followed by the application of 17 percent EDTA. The specimens received the self-etching adhesive system (XENO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. RESULTS: Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1 percent NaOCl increased the adhesive resistance significantly (p<0.001/F=22.5763). The application of 1 percent NaOCl/17 percent EDTA resulted in statistically similar µTBS to the control group. CONCLUSIONS: None of the irrigants affected negatively the µTBS of XENO III to dentin. The use of 1 percent NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1 percent NaOCl and 17 percent EDTA produced similar bond strength to that of untreated dentin.

Resistência de união à microtração de restaurações diretas e indiretas em resina composta / Microtensile bond strenght of direct and indirect composite resin restorations

O objetivo deste estudo foi avaliar a resistência de união à dentina de restaurações diretas e indiretas confeccionadas em resina composta por meio do ensaio de microtração. Trinta molares humanos hígidos tiveram suas superfícies oclusais seccionadas 2 mm abaixo das cúspides, obtendo-se superfícies planas de dentina. Os dentes foram divididos em dois grupos: G1 (restaurações indiretas), no qual a dentina foi isolada e os platôs confeccionados em resina composta foram deslocados, jateados com óxido de alimínio e posteriormente cimentados com sistema adesivo e cimento resinoso dual; G2 (restaurações diretas), no qual os platôs de resina foram confeccionados diretamente sobre a superfície dentinária com o mesmo sistema adesivo do G1. Os dentes foram seccionados, obtendo-se tres ampulhetas de cada dente (n=45/grupo). Os corpos-de-prova foram submetidos ao ensaio de microtração a 0,5mm/min. Os dados foram analisados estatísticamente pelo teste t Student (p>0,01). As médias e desvio padrão (MPa) foram: G1=22,02 (+ou- 12,47);G2=23,35 (+ou-9,82). Pode-se concluir que não houve diferença eststísticamente significativa na resistência de união à dentina de restaurações diretas e indiretas de resina composta

Effect of carisolv and papacárie on theresin-dentin bond strength in sound andcaries-affected primary molars

Aim: This study evaluated the influence of different chemomechanical caries removal techniqueson the bond strength of an adhesive system to caries-affected and healthy dentin. Methods:Thirty healthy teeth were randomly divided into three groups: Group 1 (control): no cariesremoval technique was applied; Group 2: chemomechanical technique using Carisolv®; andGroup 3: chemomechanical technique using Papacárie®Twenty caries-affected teeth were divided .into two groups: Group 4: chemomechanical technique using Carisolv; and Group 5:chemomechanical technique using Papacárie. The teeth received the application of an etch-andrinse adhesive system, were restored with composite resin, and then sectioned to obtain 4 hourglassshaped slabs from each specimen, which were subjected to a microtensile bond strength test. Datawere analyzed statistically by ANOVA and Tukey’s test (a=0.05). Results: G1 (13.387 ± 6.1074),G2 (18.123 ± 3.2611) and G3 (12.781 ± 4.5652) presented statistically significant higher meanbond strength values than the other groups (p<0.05), but did not differ significantly from each other(p>0.05). G4 (6.228 ± 5.3435) and G5 (6.482 ± 3.2076) presented the lowest mean bondstrength values and were statistically similar to each other (p>0.05). Conclusions: Neither of thechemomechanical caries removal methods interfered in the resin-dentin bond strength. However,lower tensile bond strength was found to caries-affected dentin.

Bonding to wet or dry deproteinized dentin: micro tensile bond strength and confocal laser micromorphology analysis

Aim: To investigate the influence of deproteinization and moisture condition (wet vs. dry) on the bond strength and micromorphology of resin-dentin bonding interfaces. Methods: Dentin surfaces were etched with 37% phosphoric acid for 15 s and rinsed with water. Four groups (n = 10) were tested: WET: dentin was left visibly moist; DRY: dentin was dried with compressed air; WET-D: dentin was deproteinized for 60 s using 10% NaOCl solution and left moist; DRY-D: dentin was deproteinized and dried. Prime&Bond 2.1 adhesive was applied and the teeth were restored with composite resin. Microtensile test was carried out after 24 h, and failure modes classified under magnification. Data were subjected to two-way ANOVAand Tukey’s test (P < 0.05). The bonding micromorphology was analyzed by confocal laser scanning microscopy. Results: The group DRY showed significantly lower bond strength (P < 0.05) than the other groups, which were similar to each other (P > 0.05). Adhesive failures were predominant. Analysis of micromorphology showed formation of a collagen-resin hybrid layer only for the non-deproteinizedgroups. Adhesive penetration into the dentinal tubules was deeper for the DRY-D compared to the WETD group. Conclusion: The bond strength was not dependent on the moisture condition and a more homogeneous hybridization was obtained when dentin was deproteinized.

Morphological analysis of glass, carbon and glass/carbon fiber posts and bonding to self or dual-cured resin luting agents

OBJECTIVE: The aim of this study was to evaluate the morphology of glass (GF), carbon (CF) and glass/carbon (G/CF) fiber posts and their bond strength to self or dual-cured resin luting agents. MATERIAL AND METHODS: Morphological analysis of each post type was conducted under scanning electron microscopy (SEM). Bond strength was evaluated by microtensile test after bisecting the posts and re-bonding the two halves with the luting agents. Data were subjected to two-way ANOVA and Tukey's test (α=0.05). Failure modes were evaluated under optical microscopy and SEM. RESULTS: GF presented wider fibers and higher amount of matrix than CF, and G/CF presented carbon fibers surrounded by glass fibers, and both involved by matrix. For CF and GF, the dual-cured material presented significantly higher (p<0.05) bond strength than the self-cured agent. For the dual agent, CF presented similar bond strength to GF (p>0.05), but higher than that of G/CF (p<0.05). For the self-cured agent, no significant differences (p>0.05) were detected, irrespective of the post type. For GF and G/CF, all failures were considered mixed, while a predominance of adhesive failures was detected for CF. CONCLUSION: The bonding between fiber posts and luting agents was affected by the type of fibers and polymerization mode of the cement. When no surface treatment of the post is performed, the bonding between glass fiber post and dual-cured agent seems to be more reliable.

Comparação de duas modalidades de apicectomia seguidas de retropreparo no selamento marginal de retrobturações / Comparison of two modalities of apicoectomy followed by root-end cavity preparation on marginal sealing of retrofllings

Este estudo avaliou in vitro a infltração apical após apicectomia e retrobturação, variando o ângulo de corte radicular e a técnica de preparo da cavidade retrógrada. Vinte e quatro dentes humanos unirradiculares foram tratados endodonticamente e obturados pela técnica de condensação lateral da guta-percha com cimento Endo-Fill, sendo distribuídos em dois grupos experimentais (n = 10): GI - apicectomia perpendicular ao longo eixo radicular, seguida do preparo das cavidades retrógradas com ponta ultrassônica lisa 12/90; GII - apicectomia com corte inclinado em 45° para vestibular e preparo retrógrado com broca esférica carbide em baixa rotação. Todas as retrocavidades foram seladas com cimento à base de óxido de zinco e eugenol (IRM). Os grupos experimentais foram imersos por 48 horas em solução de Rodamina B a 0,2% tamponada em ambiente com vácuo. A seguir, as raízes foram seccionadas longitudinalmente e a infiltração de corante analisada em microscópio de mensuração. O teste de U de Mann-Whitney evidenciou diferença signifcante em nível de 1% entre os grupos, com menores níveis de infiltração no grupo em que as cavidades retrógradas foram realizadas com ponta ultrassônica lisa 12/90. Pode-se concluir que a apicectomia perpendicular ao longo eixo do dente, seguida de retrocavidade confeccionada com ponta ultrassônica lisa, reduziu a infiltração apical após retrobturação com cimento a base de óxido de zinco e eugenol.

This in vitro study has evaluated the apical leakage after apicoectomy and root-end filling varying the bevel cut and the root-end cavity preparation technique. Twenty four single root human teeth were submitted to endodontic treatment and obtured by lateral condensation techique with gutta-percha points and Endo Fill cement. The teeth were distributed into two experimental groups (n = 10): Group I - perpendicular apicoectomy to root axis followed by root-end preparation performed with 12/90 smooth ultra-sonic tip. Group II - 45° buccal side inclined apicoectomy and root-end preparation performed with spherical carbide burn in low speed. All root-end cavities were sealed with zinc oxide-eugenol based cement (IRM). The experimental groups were immersed in rhodamine B dye for 48 hours and stored in vacuum environment. After that, the roots were separated longitudinally and the dye infiltration was analyzed under optical microscope. Mann-Whitney test showed signifcant difference between the groups (P < 0.01) with lowest levels of leakage in the Group I. It was concluded that the perpendicular apicoectomy followed by retrograde cavity preparation with ultra-sonic smooth tips decreases the marginal leakage in root-end cavities sealed with zinc oxide-eugenol cement.

Influência do tempo de fotoativação na resistência à flexão de compósitos restauradores / Influence of photoactivation time on flexural strength of restorative composites

Este estudo avaliou a influência de dois tempos de fotoativação sobre a resistência à flexão de quatro compósitos comerciais. Amostras em forma de barra (25 mm x 2 mm x 2 mm) foram confeccionadas em matriz de aço inoxidável de acordo com s ISO 4049 e fotoativadas com um aparelho LED com cinco ativações de 20 ou 60s, em diferentes pontos ao longo das superfícies de topo e base da amostra. O teste foi realizado em uma máquina de ensaios mecãnicos com velocidade de 0,05 mm/min. As médias (MPa) foram submetidas à análise de variância de dois fatores e ao teste de Tukey (p < 0,05). Em ambos os tempos de fotoativação, os compósitos Filtek Supreme® e Esthet-X® apresentaram os maiores valores de resistência à flexão. O compósito Opallis® apresentou valores intermediários com 20s de ativação, diferindo estatisticamente do compósito 4 Seasons® com a menor média. Com 60s de ativação, os compósitos Opallis® e 4 Seasons® obtiveram médias significativamente menores que os demais, mas não diferiram entre si. Todos os compósitos apresentaram aumento significativo dos valores de resistência à flexão com o aumento do tempo de ativação. Concluiu-se que a fotoativação por 60s aumentou os valores de resistência à flexão dos compósitos.

Influência da profundidade dentinária na resistência à microtração de sistemas adesivos de condicionamento ácido total e autocondicionante / Influence of dentin depth on microtensile bond strength of total etching and self-etching adhesive systems

Objetivo: O objetivo deste estudo foi avaliar a resistência de união à microtração de um sistema adesivo monocomponente (Single Bond - SB) e de um sistema adesivo autocondicionante (XENO III - XN) em dentina superficial (DS) e em dentina profunda (DP). Metodologia: A face oclusal de vinte molares humanos hígidos foi seccionada em dois níveis: 1 mm abaixo das cúspides (DS) e 3 mm abaixo das cúspides (DP). Os dentes foram divididos em 4 grupos: G1 (controle 1): SB e dentina DS, G2 (controle 2): SB e dentina DP, G3: XN e dentina DS, e G4: XN e dentina DP. Um bloco de resina composta foi confeccionado sobre essas superfícies. Os dentes foram seccionados obtendo-se quatro corpos-de-prova em forma de ampulheta de cada dente (n=20/grupo). Os corpos-de-prova foram submetidos ao ensaio de microtração à velocidade de 0,5mm/min. Os dados foram analisados por ANOVA e teste de Newman Keuls. Resultados: As médias (desvio-padrão) foram (em MPa): G1 = 15,84 (4,04)a; G2 = 13,84 (3,52)a; G3 = 8,76 (1,61)b; G4 = 8,64 (3,12)b. Conclusão: Conclui-se que diferentes níveis de profundidade dentinária não afetaram a resistência de união para o mesmo material; SB mostrou os maiores valores em ambas as profundidades dentinárias.

Purpose: The aim of this study was to evaluate the microtensile bond strength of one monocomponent adhesive system (Single Bond - SB) and one self-etching adhesive system (XENO III - XN) in superficial (SD) and deep (DD) dentin.Methods: The occlusal surface of twenty sound human molars was sectioned in two levels: 1mm (SD) and 3mm (DD) below the cusps. The teeth were divided into four groups: G1 (control 1): SB and SD dentin, G2 (control 2): SB and DD dentin, G3: XN and SD dentin, and G4: XN and DD dentin. One composite block was built over these surfaces. The teeth were sectioned into four slabs, which were trimmed to hourglass-shaped specimens (n=20 specimens/group). Each specimen was subjected to microtensile bond testing at a crosshead speed of 0.5mm/min. Data were analyzed by ANOVA and Newman Keuls test. Results: Means (standard deviation) values were (in MPa): G1 = 15.84 (4.04)a; G2 = 13.84 (3.52)a; G3 = 8.76 (1.61)b; G4 = 8.64 (3.12)b. Conclusion: It may by concluded that different depth levels of dentin do not affect bond strength for the same material; SB showed the highest bond strength values in both dentin depths.

Influência da desproteinização e da umidade sobre o substrato dentinário na microinfiltração em restaurações de resina composta / Influence of deproteinization and of wet on the dentinal substratum on microleakage in composite restorations

O objetivo deste estudo foi verificar a influência da desproteinização e da condição do substrato dentinário (úmido ou seco) na microinfiltração marginal em restaurações com resina composta. Oitenta cavidades classe V, preparadas em quarenta terceiros molares humanos (Banco de dentesa FO-UPF), com margem gengival em dentina foram divididas aleatoriamente em quatro grupos: G1 (controle) - sistema adesivo (Prime & Bond 2.1®, Dentsply) aplicado à dentina úmida; G2 - sistema adesivo aplicado à dentina seca; G3 - dentina desproteinizada com hipoclorito de sódio (NaOCl 10 por cento, 60s) e o sistema adesivo aplicado à dentina úmida; G4 - dentina desproteinizada e o sistema adesivo aplicado à dentina seca. Após restaurados, os espécimes foram termociclados, isolados, imersos em corante, incluídos em resina acrílica e seccionados. Para a análise das secções foi utilizado um microscópico óptico e os escores tabulados. Os dados foram submetidos à análise estatística (Kruskal Wallis/1por cento;Ho=0,69 por cento), sendo que G3 e G4 apresentaram diferença estatística entre si. Os demais grupos não apresentaram diferença estatísticamente significativa quando correlacionados. Nas condições experimentais foi possível concluir que a camada de colágeno não tem influência na infiltração marginal. Um índice de microinfiltração significativamente menor foi encontrado após a remoção do colágeno para o substrato dentinário seco

Tratamento de perfuração e de lesão de furca com barreira de CIV e RC / Furcation perforation treatment with modified ionomer barrier

O objetivo deste trabalho foi apresentar uma técnica para manutenção de dentes com perfuração radicular. Esta técnica envolve a remoção da raiz mésio-vestibular do primeiro molar superior esquerdo com perfuração no assoalho da câmara pulpar e vedamento da perfuração com um tampão de cimento de ionômero de vidro. O dente foi restaurado com resina composta e, para estabelecer uma união com o dente vizinho, associou-se tiras de polietileno. Essa medida visou proteger e estabilizar o remanescente do elemento 26 das cargas oclusais. O prognóstico dos dentes tratados por ressecção radicular é crítico, porém pode ser melhorado com adequada seleção do caso e tratamento periodontal, endodôntico e restaurador bem planejados.

Análise da influência de três métodos de pós-polimerização sobre a resistência à flexão de um compósito de uso clínico / Influence analisys of three pos-polymerization methods in relation t flexural strenght of a clinical composite

O objetivo desse trabalho foi avaliar a resistência à flexão de uma resina composta microhíbrida fotopolimerizável submetida a três métodos de pós-polimerização. Foram confeccionadas 40 barras de resina A2, seguindo as especificações da ISO 4049, fotopolimerizadas por 40 segundos e em seguida divididas em quatro grupos: G1 - controle negativo, que não recebeu pós-polimerização; G2 - controle positivo, polimerizadora laboratorial EDG Lux - luz e calor (7 minutos; 600mW/cm²); G3 - ciclo de autoclave - calor e pressão (25 minutos; T=138°C; P=2,58bar); G4 - ciclo em microondas - calor (3 minutos/1800 Watts). O teste de resistência flexural foi realizado em máquina de ensaio EMIC DL 2000 com velocidade de 0,5mm/min. Aos resultados obtidos foi aplicada a fórmula σ=3FI/ 2db², para obter os valores de resistência flexural em MPa. As médias dos grupos foram: G1=97,49MPa, G2=94,62MPa, G3=122,22MPa e G4=108,21MPa, não apresentando diferença estatisticamente significante ao nível de 5%.

Resistência à microtração de pinos de fibra de vidro em função do tratamento de superfície / Microtensile strength of fiberglass posts in function of the surface treatment

Este estudo in vitro avaliou a resistência à microtração de pinos pré-fabricados de fibra de vidro submetidos a diferentes métodos de preparo de superfície. Foram selecionados 40 pinos de fibra de vidro seccionados na metade do comprimento. As secções dos pinos foram refixadas com sistema adesivo fotopolimerizável e cimento resinoso dual. Para o correto posicionamento das extremidades do pino, foi utilizado um suporte metálico em forma de canaleta. Antes da aplicação do sistema adesivo, as extremidades receberam os seguintes tratamentos: GI - (controle) sem tratamento prévio; GII - silano; GIII - condicionamento com ácido fosfórico 37%; GIV - jato com óxido de alumínio (50µm); GV - ácido + silano; GVI - jateamento + ácido; GVII - jateamento + silano; GVIII - jateamento + ácido + silano. Após a união das extremidades os pinos foram fixados ao suporte da máquina universal de ensaios (0,5 mm/min e célula de carga de 5kgF) e submetido ao teste de microtração. Os dados foram submetidos à análise de variância e teste Duncan (α=5%), que demonstrou diferença estatística quando foram comparados grupos com silano vs grupos sem silano. Outras interações não demonstraram diferença estatística. Foi possível concluir que a silanização ou a associação deste tratamento com outros tratamentos resultaram em um aumento da resistência de união, comparada a dos grupos onde o silano não foi utilizado

Uma alternativa estética com prótese fixa livre de metal / An esthetic choice with metal-free fixed prosthesis

Atualmente, a procura dos pacientes por um tratamento dentário de maior qualidade e durabilidade, intensificada pelos sorrisos perfeitos apresentados na mídia, tem imposto à odontologia estética um grande desafio. Este trabalho tem o objetivo de informar sobre um dos sitemas para prótese sem metal, os cerômeros, que são polímeros otimizados com cerâmica e reforçados com fibras. Esses materiais apresentam várias marcas, entre as quais o sistema targis-Vectris, utilizados nas clínicas para a confecção de restaurações unitárias e pontes de pequena extensão. O artigo informa a composição e propriedades desses materiais, assim como sua utilização na prática clínica, com apresentação de um caso clínico

Utilizaçäo clínica de cimentos ionoméricos híbridos como dentina artificial / clinical use of hybrid ionomers cements as dentin substitutes

O objetivo desse trabalho é relatar um caso clínico, no qual foi utilizado um cimento de ionômero de vidro modificado por resina como suporte para o esmalte socavado, tendo a funçäo de dentina artificial, para posteriormente ser restaurado com amálgama de prata. Devido a esse procedimento, o preparo cavitário realizado foi mais conservador, ao mesmo tempo que se promoveu um esforço das estruturas dentais, as quais se encontravam friáveis

Resistência ao cisalhamento da uniäo entre adesivo e dentina / Shear bond strength of union between bonding agent and dentin

O objetivo deste trabalho foi avaliar a resistência ao cisalhamento entre a resina e substrato dentinário, empregando-se dois sistemas adesivos: Pro Bond (Caulk Dentsply) e Scotchbond MP+ (3M). Confeccionaram-se vinte corpos de prova, divididos em dois grupos (A - Pro Bond e B-SMP+), que foram submetidos ao teste de cisalhamento. Pela análise estatística dos resultados, concluiu-se que os sistemas adesivos apresentaram resultados estatisticamente semelhantes no subtrato dentinário, onde a média dos valores do grupo A foi de 7,27 Mpa e a do grupo B, de 6,96 MPa